海岸實體暴露 12 個月12-month coastal exposure
無膨脹、龜裂、剝離No swelling, cracking, or peeling
JIS K 5600-7-6｜日本塗料檢查協會｜No.215134｜2022
試片表面有透明保護塗層；戶外應用以該塗層為前提。Specimens used a transparent protective coating; exterior use requires that coating.
Evidence Library · Updated 2026-10
檢測報告中心Test-report center
本頁整理 19 份由日本 GBRC、JTTA、日本塗料檢查協會、BOKEN、Eurofins、中國 CTC 與 Southern LCS 等機構出具的試驗報告；每筆均標示標準、樣品條件與適用限制。This page organizes 19 third-party test reports from laboratories including GBRC, JTTA, JPIA, BOKEN, Eurofins, CTC, and Southern LCS, with standards, specimen conditions, and limits stated for each result.
15 份石材報告stone reports5 份 Anova Core™ 報告Anova Core™ reportsPDF 直接查閱PDF access
查找報告Find a report
依產品系統篩選Filter by material system
PDF · No.215134
促進耐候 500 h500-hour accelerated weathering
變色等級 2Color-change grade 2
JIS K 5600-7-7｜日本塗料檢查協會｜No.215133｜2021
尺寸穩定 –20～90℃Dimensional stability, –20 to 90℃
尺寸變化率 0.0%Dimensional change 0.0%
JIS S 2029 準用｜日本 BOKEN｜25023003293｜2023
熱衝擊Thermal shock
135℃ 後無裂紋（n = 5）No cracks after 135℃ test (n = 5)
JIS A 1509-7｜JTTA｜22-0434｜2022
耐凍融Freeze-thaw resistance
100 循環後，5 片試料皆無損傷Five specimens undamaged after 100 cycles
JIS A 1509-9:2014｜JTTA｜22-0435｜2022
乙酸鹽霧 200 h200-hour acetic salt spray
外觀無明顯變化No obvious visual change
GB/T 10125-2012｜中國 CTC｜WT2015B07N00342｜2015
吸水率Water absorption
平均 1.16%（1.01–1.44%）Average 1.16% (1.01–1.44%)
JIS A 1509-3｜JTTA｜22-0432｜2022
耐磨耗Abrasion resistance
127–179 mm³
JIS A 1509-5｜JTTA｜22-0433｜2022
防滑Slip resistance
C.S.R・B 0.58–0.85；C.S.R 0.59–0.62
JIS A 1509-12｜JTTA｜22-0437｜2022
不建議用於商業公共通道地坪。Not recommended for commercial public circulation floors.
耐藥品性Chemical resistance
強鹼：5 片中 4 片有變化Strong alkali: change in four of five specimens
JIS A 1509-10:2020｜JTTA｜22-0436｜2022
避免強鹼清潔劑。Avoid strong-alkali cleaners.
甲醛釋出量（八系列）Formaldehyde emission (eight series)
< 0.1／0.1／0.2 mg/L
JIS A 1460（デシケーター法）｜岡山縣工業技術中心｜No.190／191／297／298／327／328／329／330｜2017–2018
REACH SVHC
219 項全數未檢出All 219 substances not detected
EU REACH（ECHA Candidate List, 219 SVHC）｜Eurofins 深圳｜EFSN21070683C-C1｜2021｜中文版Chinese version
可溶性元素遷移Migration of soluble elements
PASS
EN 71-3:2019｜Eurofins 深圳｜EFSN21070683C-C3｜2021｜中文版Chinese version
燃燒性能Reaction to fire
B1（C-s2, d0, t0）
GB 8624-2012（中國標準）｜中國 CTC｜WT2023B03A00518｜2023
僅適用於 2.5 mm 柔性石材背貼 12 mm 矽酸鈣板之受測構成；台灣 CNS 6532 尚未取得。Applies only to the tested 2.5 mm stone and 12 mm calcium-silicate-board assembly; Taiwan CNS 6532 has not been obtained.
LumiSlate LED 燈具電氣安全LumiSlate LED luminaire electrical safety
屋內用燈具測試合格Indoor luminaire passed testing
J60598-1／J60598-2-1／J55015｜Southern LCS｜LCSB11055009S｜2025
檢查成績書，受測燈具為屋內用。Test report covering an indoor luminaire.
架高隔音地板樓板衝擊音Raised-floor impact-sound test
ΔLL(Ⅱ)-3S／ΔLH(Ⅱ)-3S
JIS A 1440-1／-2｜日本 GBRC｜IVA-26-0082E｜2026
完成面高度 173.5 mm 的完整構造試體，不可直接套用至單芯板。Complete 173.5 mm-high test assembly; not transferable to the core board alone.
甲醛（日本）Formaldehyde (Japan)
< 0.1 mg/L
JIS A 1460:2021｜日本 GBRC｜VD-26-0012｜2026
平均與最大值皆低於定量下限。Both average and maximum were below the quantification limit.
甲醛（中國）Formaldehyde (China)
未檢出（< 0.10 mg/L）Not detected (< 0.10 mg/L)
GB/T 17657-2022 乾燥器法｜中國 CTC｜WT2023B01A05265｜2023
空氣聲隔聲（單芯板 52 mm）Airborne sound insulation (52 mm board)
Rw(C;Ctr) = 30(-2;-3) dB
GB/T 19889.3-2005｜中國 CTC｜WT2023B03A01247｜2023｜面密度 14 kg/m²surface mass 14 kg/m²
型錄下載Catalogues
規格、系列與選材資料Specifications and material selection
石材型錄 V61・電腦版Stone catalogue V61 · desktop
PDF · 19.3 MB · 2026-10
下載Download石材型錄 V61・手機版Stone catalogue V61 · mobile
PDF · 11.8 MB · 2026-10
下載DownloadAnova Core™ 降噪蛋殼芯板型錄 V22.1Anova Core™ Natural-Fiber Eggshell Core Board catalogue V22.1
PDF · 8.0 MB
下載Download本頁數據為原廠 NALEXIBLE 委託第三方機構之試驗結果，僅代表受測樣品於該試驗條件下之表現；實際性能依系列、厚度、基材、表面處理與施工條件而異。LED 燈具報告為中國深圳 Southern LCS 實驗室依日本電氣用品安全法技術基準測試之檢查成績書，受測燈具為屋內用。2026 年 10 月版。GBRC 報告之引用以 GBRC 書面同意為前提。These results were commissioned by NALEXIBLE from third-party laboratories and apply only to the tested specimens and conditions. Actual performance varies by series, thickness, substrate, surface treatment, and installation. The LED document is an indoor-luminaire test attestation issued by Southern LCS in Shenzhen against Japanese technical requirements. October 2026 edition. Citation of GBRC reports is subject to GBRC written consent.